Product Brief Introduction
Product name: ABS Resins
CAS: 9003-56-9
MF: (C8H8)x·(C4H6)y·(C3H3N)z
MW: 633.91
Product Specification
|
Melt Flow Rate (220°C/10kg) |
21g/10min |
|
Specific Gravity (23℃) |
1.03 |
|
Molding Shrinkage |
0.4% ~ 0.7% |
|
Tensile Strength 3.2mm (50mm/min) |
500kg/cm2 |
|
Tensile Elongation 3.2mm (50mm/min) |
25.0% |
|
Flexural Strength 6.4mm (15mm/min) |
700kg/cm2 |
|
Flexural Modulus 6.4mm (15mm/min) |
22000kg/cm2 |
|
IZOD Impact Strength 6.4mm |
23℃: 23 kg.cm/cm |
|
-30℃: - |
|
|
Rockwell Hardness (R-Scale) |
109 |
|
Heat Deflection Temperature, 6.4mm (Unannealed, 18.6kg) |
87.0℃ |
|
Vicat Softening Temperature (1kg) |
95.0℃ |
|
Flammability (1.5mm) |
HB class |
|
Drying Point |
75.0℃ ~ 85.0℃ |
|
Drying Time |
2hrs ~ 4hrs |
|
Cylinder Temperature |
Rear: 180.0℃ ~ 200.0℃ |
|
Middle: 190.0℃ ~ 210.0℃ |
|
|
Front: 200.0℃ ~ 220.0℃ |
|
|
Nozzle Temperature |
200.0℃ ~ 230.0℃ |
|
Melt Point |
210.0℃ ~ 240.0℃ |
|
Mold Temperature |
40.0℃ ~ 70.0℃ |
|
Injection Pressure |
Injection Pressure: 60.0MPa ~ 100.0MPa |
|
Holding Pressure: 70.0MPa ~ 90.0MPa |
|
|
Back Pressure: 0.5MPa ~ 1.0MPa |
|
|
Screw Rotate Speed |
30.0%~60.0% |